Fluon® ETFE Film
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | Asahi Glass Co., Ltd. |
| Trademark: | Fluon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HIMxrN_Fluon-ETFE-Film.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fluon® ETFE Film is an Ethylene Tetrafluoroethylene Copolymer (ETFE) product. It is available in North America. Typical application: Film. Primary characteristic: chemical resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 39.0 | MPa | JIS K7127 |
| Tensile Elongation (Break) | 200 to 510 | % | JIS K7127 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 150 to 180 | °C | |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 9.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 120 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.60 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 6.0E-4 | ||
| 1 kHz | 8.0E-4 | ||
| 1 MHz | 5.0E-3 | ||
| 1.00 GHz | 0.010 | ||
| Arc Resistance | 120 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RENOL® Engineering Resin Color Masterbatch | Clariant Corporation | TP, Unspecified | RENOL® |
| Vitaster® US30WT6184 | Jackdaw Polymers | PBT | Vitaster® |
| CALP 8900R | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Evolue™ SP3010 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Hifax CA1110/2AC | LyondellBasell Industries | TPO (POE) | Hifax |