ALCUDIA® EVA PA-537
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HIIS3D_ALCUDIA-EVA-PA-537.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA copolymer ALCUDIA® PA-537 is suitable for film extrusion applications. This material combines easy processability with excellent mechanical and optical properties. It contains antioxidant additives. TYPICAL APPLICATIONS
Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.941 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 18.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 100 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 31.0 | MPa | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 32.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 800 | % | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 900 | % | ISO 527-3 |
| Dart Drop Impact (100 µm, Blown Film) | > 1400 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 100 µm, blown film | 2.4 | N | ISO 6383-2 |
| TD : 100 µm, blown film | 3.4 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.0 | °C | ISO 306/A |
| Melting Temperature | 87.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (100 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 100 µm thickness film, blow up ratio 2. 5:1, frost line height 50 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8240-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Gallonprene® GP210-5502L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Huafon HF-3492A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Karina BLUE COLOR CONCENTRATE 06/183-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8820H Purple 8424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |