BJB Polyurethane TC-851 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HI0P5w_BJB-Polyurethane-TC-851-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-851 A/B produces a high impact rigid 78 Shore D material that is commonly used to make computer housings, models of all kinds, artwork, and can also be used for electronic component encapsulation. It provides a working time of 8 minutes. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.07 | g/cm³ | |
| -- 2 | 1.11 | g/cm³ | |
| -- | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 3 | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 - 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ASTM D638 |
| Tensile Strength | 49.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 96.1 - 102 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 87.8 - 93.3 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 50, mixing ratio by capacity: 52 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| 25°C 4 | 1400 | cP | Brookfield |
| 25°C 5 | 75.0 | cP | Brookfield |
| 25°C 6 | 400 | cP | Brookfield |
| Demold Time (25°C) | 60 - 120 | min | |
| Work Time 7(25°C) | 6.0 - 8.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day | |
| Note: Reported physical properties are based on test specimens cured at an elevated temperature, 180°F (82°C).In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 150-180°F (66-82°C). Support of the part may be required to prevent part deformation during the heat curing process. |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 12" x 1/2" x 1/2" |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Mixed |
| 7 . | 100g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86020-85UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polyethylene LDPE 1200 MN 18 C | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Brush-On® 50 | Smooth-On, Inc | PUR, Unspecified | Brush-On® |
| CYCOLOY™ NX07353 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| EnCom PC-ABS 1310 | EnCom, Inc. | PC+ABS | EnCom |