LNP™ THERMOCOMP™ HB006 compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HHorVq_LNP-THERMOCOMP-HB006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead. Also known as: LNP* THERMOCOMP* Compound HB-1006 Product reorder name: HB006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.27 | g/cm³ | ASTM D792 |
| -- | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.7 | % | |
| Across Flow : 24 hr | 1.5 | % | |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1970 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.5 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Break | 43.4 | MPa | ASTM D638 |
| Break | 41.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 23 | % | ASTM D638 |
| Yield | 24 | % | ISO 527-2 |
| Break | 20 | % | ASTM D638 |
| Break | 43 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1920 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.2 | MPa | ASTM D790 |
| -- | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 3 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 33.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 151 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 46.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 47.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 227 to 260 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE F654 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Zhongfa PET G30FR | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| Fainplast PVC PHT 0144 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Fainplast PVC PM 6510/K | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hanwha Total PP GB72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |