LNP™ LUBRICOMP™ DX96651 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HGdXQ1_LNP-LUBRICOMP-DX96651-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DX96651 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-D-96651 SF Product reorder name: DX96651 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.75 | % | ISO 294-4 |
| Flow : 24 hr | 0.73 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2210 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 48.5 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2 |
| Break | 58.6 | MPa | ASTM D638 |
| Break | 46.8 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2480 | MPa | ASTM D790 |
| -- | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 93.5 | MPa | ASTM D790 |
| -- | 90.7 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 2 | 9.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 41.0 | J | ASTM D3763 |
| -- | 128 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 140 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.6E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® ABS 350C | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS+PVC | SILVER® |
| Tisoplen® PPH 25 GFR FR | Tisan | PP Homopolymer | Tisoplen® |
| Xuchuan XCG-100 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DENILEN M 2013 | Vamp Tech | PP, Unspecified | DENILEN |
| TECHNYL® C 502XT NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |