RTP 2288 LF
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HGVFCh_RTP-2288-LF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 37900 | MPa | ASTM D638 |
| Tensile Strength | 296 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.2 | % | ASTM D638 |
| Flexural Modulus | 31700 | MPa | ASTM D790 |
| Flexural Strength | 434 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 910 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 1mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 357 - 399 | °C | |
| Middle Temperature | 357 - 399 | °C | |
| Front Temperature | 357 - 399 | °C | |
| Mold Temperature | 149 - 204 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP2380 | LyondellBasell Industries | PP Random Copolymer | Moplen |
| WanBlend® WHT-8185M | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| NEOFLON™ NP-130 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |
| Optix® CA-87 | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| Alpha PVC 3006-95 | Mexichem Specialty Compounds Inc. | PVC, Unspecified | Alpha PVC |