Generic PPE+PS+PP
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HGLR3L_Generic-PPE-PS-PP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+PS+PP This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.987 - 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 11 - 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.65 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1170 - 1710 | MPa | ASTM D638 |
| 23°C | 1660 - 1760 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 33.8 - 43.8 | MPa | ASTM D638 |
| Yield, 23°C | 33.9 - 44.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 27.6 - 41.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 6.5 - 15 | % | ASTM D638 |
| Fracture, 23°C | 83 - 200 | % | ASTM D638 |
| Fracture, 23°C | 46 - 120 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1340 - 1560 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 49.0 - 53.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 - 590 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C) | 36.2 - 45.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 - 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 - 92.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 85.0 - 146 | °C | ASTM D1525 |
| -- | 102 - 118 | °C | ISO 306 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 8.1E-5 - 1.6E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 7.2E-5 - 1.1E-4 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 62.5 - 62.8 | °C | |
| Rear Temperature | 250 - 252 | °C | |
| Middle Temperature | 260 - 263 | °C | |
| Front Temperature | 268 - 270 | °C | |
| Nozzle Temperature | 274 - 275 | °C | |
| Processing (Melt) Temp | 274 - 275 | °C | |
| Mold Temperature | 40.6 - 50.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PS+PPThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC5UVZ (Series: UV/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Unichem 9811A-03 | Colorite Polymers | PVC, Unspecified | Unichem |
| DJSilicone NE--D-2/NE-D-2U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| ENFLEX S4065A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Polyrocks EP8400XD125VH-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |