SWANCOR Epoxy 905C

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	SWANCOR IND. CO., LTD.
Trademark:	SWANCOR Epoxy
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HFGHUb_SWANCOR-Epoxy-905C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

SWANCOR 905C is a brominated Bisphenol A type epoxy vinyl ester resin. It provides excellent corrosion resistance to a broad range of organic and inorganic acids, alkali, oxidizing chemicals and salt solutions etc as good as Bisphenol A type resins. It also provides very good mechanical strength such as tensile and flexural while incorporated with reinforcement such glass fiber, carbon fiber or kevlar fiber etc. SWANCOR 905C offers excellent flame retardancy for FRP applications. ASTM E84 Class 1 can be achieved while incorporated with Nyacol APE 3040. It is also designed to provide superior toughness with excellent fatigue resistance due to high heat distortion temperature.

General Information
Features	Good corrosion resistance Good strength Fatigue resistance Heat resistance, high Good toughness Flame retardancy
Uses	Floor maintenance/repair Industrial water tank Piping system Military application
Agency Ratings	FDA 21 CFR 177.2420 2
Appearance	Transparent amber
Forms	Liquid
Processing Method	Filament power winding Casting Sprayable pultrusion Hand coating Resin transfer molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity ¹	1.15	g/cm³

Hardness	Nominal Value	Unit	Test Method
Barcol Hardness	35		ASTM D2583

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3100	MPa	ASTM D638
Tensile Strength	82.7	MPa	ASTM D638
Tensile Elongation (Break)	5.0 - 6.0	%	ASTM D638
Flexural Modulus	3410	MPa	ASTM D790
Flexural Strength	134	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	111	°C	ASTM D648

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	23	%	ASTM D2863

Thermoset	Nominal Value	Unit	Test Method
Shelf Life (25°C)	26	wk

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (25.0°C)	0.300 - 0.450	Pa·s	ASTM D3835

Additional Information
Solid Content: 65.0 ± 1.5%Gel Time: 15 to 25 min

Note Message
1 .	± 0.02

Resin Grade	Manufacturer	Category	Trademark
Miramid® SP10S	BASF Leuna GmbH	Nylon 66	Miramid®
New-prene™ 8380B	Total Polymer Vision (Suzhou) Co., LTD	PP+EPDM	New-prene™
GAPEX® RPP20EU34WH	Ferro Corporation	PP, Unspecified	GAPEX®
HydroMed™ D2	AdvanSource Biomaterials Corp.	PUR-Ether	HydroMed™
LNP™ THERMOCOMP™ PF006 compound	SABIC Innovative Plastics	Nylon 6	LNP™ THERMOCOMP™