DOMAMID® A1-009-V25-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HFFLHq_DOMAMID-A1-009-V25-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, medium viscosity, 25% glass fiber reinforced, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 46.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 0.90 | % | |
| Flow : 23°C, 72 hr | 0.30 | % | |
| Water Absorption 2 | ISO 62 | ||
| Saturation, 23°C | 1.9 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 25 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 155 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus 3 | 6100 | MPa | ISO 178 |
| Flexural Stress 4 | 235 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 203 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 199 | °C | ISO 306/B50 |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | VDE 0303-3 |
| Volume Resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(2.00 mm) | 41 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | VDE 0471/2 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 24 hrs |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoDur PBT 4 GF10 black (9992) | TechnoCompound GmbH | PBT | TechnoDur |
| TECHNYL® A 218 V25 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| MORETEC™ 0358CN | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| Utomer UT356 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Iupilon® EGN2040DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |