Ecomass® 3800ZD82
| Category: | PMP , Polymethylpentene |
| Manufacturer: | Ecomass Technologies |
| Trademark: | Ecomass® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HEkFca_Ecomass-3800ZD82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ecomass® 3800ZD82 is a Polymethylpentene (PMP) material filled with tungsten. It is available in North America for injection molding. Important attributes of Ecomass® 3800ZD82 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.89 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3170 | MPa | ASTM D638 |
| Tensile Strength | 16.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 2220 | MPa | ASTM D790 |
| Flexural Strength | 14.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 91.7 | °C | |
| 1.8 MPa, Unannealed | 94.4 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 274 to 302 | °C | |
| Mold Temperature | 57.2 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound BH3020NH | Samyang Corporation | PC | TRIREX® Compound |
| FLEXITEQ™ F60A111UV | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| ELASTOSIL® M 4514 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| Kumho PS HI 425EP | Korea Kumho Petrochemical Co., Ltd. | PS (HIPS) | Kumho PS |
| MAJORIS FN020 - NATFL | AD majoris | PP Homopolymer | MAJORIS |