Veroplas PA2009L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Veroplas |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HEPf0i_Veroplas-PA2009L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Veroplas PA2009L is a polyamide 6 (nylon 6) product,. It can be processed by injection molding and is available in North America or Europe. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 68.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 77.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 48.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 171 | °C | ASTM D1525 |
| Additional Information |
|---|
| Glow Wire Test, UNE 20-672-83: 1200°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.17 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 25 FRA 5 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TOTAL Polyethylene HDPE D4720 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| XANTAR® 24 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Hylon® N1033STHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Polimid A 25 GF V0A TR1 | Poliblend S.p.a. | Nylon 66 | Polimid A |