SNOLEN® EB 0.41/53
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HEHbuo_SNOLEN-EB-0-41-53.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES Good impact strength.Good environmental stress cracking resistance. MAJOR APPLICATIONS Containers. Cans. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.949 to 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 7.5 to 12 | g/10 min | |
| 190°C/5.0 kg | 0.29 to 0.41 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(80°C, 2% Arkopal) | 7.00 | hr | ISO 16770 |
| Melt Flow Ratio | 24.0 to 30.0 | ||
| Swelling | 95 to 130 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1050 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 24.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | > 800 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 84.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | @ 3.5 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6610/80 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Genestar™ G1352A-M41 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| KEBAFLEX® SG 55 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| LG ASA LI968W | LG Chem Ltd. | ASA | LG ASA |
| MAJORIS CT403 - 8229 | AD majoris | PP, Unspecified | MAJORIS |