LNP™ THERMOCOMP™ Noryl_FM4025 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HDnVIw_LNP-THERMOCOMP-Noryl-FM4025-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP NORYL_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250" wall thickness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.29 | g/cm³ | ASTM D792 |
| -- | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 6.40mm | 0.15 | % | Internal method |
| Transverse flow : 3.20mm | 0.25 | % | Internal method |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Foam - Physical 2 | 10 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Mechanical 3 | 10 | % | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Impact 4 | 10 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Thermal 5 | 10 | % | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Electrical 6 | 20 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Flame Class Minimum Density | 1.260 | g/cm³ | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weight Reduction | 10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 6.35 mm) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 6.35 mm) | 1.5 | % | ASTM D638 |
| Flexural Modulus (6.40 mm) | 7930 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 121 | MPa | ASTM D790 |
| Poisson's Ratio | 0.38 | ASTM D638 | |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-static | 0.52 | ASTM D1894 | |
| With Self-Static | 0.55 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 100 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 118 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 95°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 95°C | 3.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Arc Resistance 7 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.90 mm | V-1 5VA | UL 94 | |
| 5.00 mm | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Structural Foam Molding - Blowing Agent, Physical System: Nitrogen GasStructural Foam Molding - Concentration Range (Blowing Agent): 1 - 3 %Structural Foam Molding - Drying Temperature (Resin): 104 - 110 °CStructural Foam Molding - Drying Time (Resin): 2 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 8 hrsStructural Foam Molding - Front Temperature: 271 - 304 °CStructural Foam Molding - Melt Temperature: 271 - 310 °CStructural Foam Molding - Middle Temperature: 271 - 304 °CStructural Foam Molding - Mold Temperature: 66 - 82 °CStructural Foam Molding - Nozzle Temperature: 271 - 304 °CStructural Foam Molding - Rear Temperature: 260 - 288 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 2 % |
| Note Message | |
|---|---|
| 1 . | Foam molded |
| 2 . | 6.4 mm wt reduction |
| 3 . | 6.4 mm wt reduction |
| 4 . | 6.4 mm wt reduction |
| 5 . | 6.4 mm wt reduction |
| 6 . | 6.4 mm wt reduction |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® M/MX 50 | A. Schulman Europe | PC+PBT | SCHULABLEND® |
| Shandong PA610 A6G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 610 | Shandong PA610 |
| TEKNIFLEX® VDC 300-60 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PVDC | TEKNIFLEX® |
| UBESTA 3020 X15 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Zytel® 73G30TGI BK267 | DuPont Performance Polymers | Nylon 6 | Zytel® |