STERLENE™ HMU210
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HCOC6v_STERLENE-HMU210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ HMU210 is a compounded mineral filled polypropylene (TPO) for injection molding, characterised by good dimensional stability and good heat resistance, suitable for automotive underhood application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.034 | % | Internal Method |
| Ash Content 2(600°C) | 20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 6.5 | % | |
| Break, 23°C | 25 | % | |
| Flexural Modulus 3(23°C) | 2440 | MPa | ISO 178 |
| Flexural Stress 4(23°C) | 47.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Complete Break) | 4.6 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 87.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 30 min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 85°C x 2hr anneal |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® MV 10 R | Versalis S.p.A. | LDPE | Riblene® |
| Evermore PUR SA-6066 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| EL-Lene™ H455JA | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Karina BLACK PVC COMPOUND CAK 75-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8600-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |