LNP™ STAT-KON™ Lexan_JK2500 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HCBzKt_LNP-STAT-KON-Lexan-JK2500-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON LEXAN_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.060 to 0.15 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 11100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 63.8 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/5 |
| Break 3 | 63.8 | MPa | ASTM D638 |
| Break | 63.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.3 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 2.4 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9240 | MPa | ASTM D790 |
| -- 7 | 10100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 110 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 9 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 220 | J/m | ASTM D4812 |
| 23°C 10 | 15 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 14.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 98.3 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 93.9 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 96.1 | °C | |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ASTM D1525 11 |
| -- | 100 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 2.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.991 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 260 to 277 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 271 to 299 | °C | |
| Nozzle Temperature | 271 to 299 | °C | |
| Processing (Melt) Temp | 271 to 310 | °C | |
| Mold Temperature | 48.9 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 35 to 75 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ H15SQ9 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| Tislamid® PA66 PA66 30 GFR EP | Tisan | Nylon 66 | Tislamid® PA66 |
| Chemical Resources ABS1200 | Chemical Resources, Inc. | ABS | Chemical Resources |
| Epic Epoxy S7512 | Epic Resins | Epoxy | Epic Epoxy |
| TechnoFiber Performance PP LGF 20-10-02 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber Performance |