ASTALAC™ ABS M35AS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HBYebB_ASTALAC-ABS-M35AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALAC™ ABS M35AS is a high flow, anti-static, medium impact ABS injection moulding grade offering an excellent balance of impact toughness, product rigidity, heat resistance and easy mouldability. Applications include general purpose mouldings including thin wall sections and long flow paths. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 34 | g/10 min | |
| 230°C/3.8 kg | 10 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2150 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 76.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 80.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 88.0 | °C | |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Buna® EP T 5459 CL | LANXESS Corporation | EPDM | Buna® EP |
| DOMAMID® 66/6V0M | DOMO Engineering Plastics SPA | Nylon 66/6 | DOMAMID® |
| KOPELEN J-380A | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Lushan EF528T | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |
| NYLOY® KF-0010N 6121W1 | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |