Rynite® 530 NC010
| Category: | PET , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Rynite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HBFBB0_Rynite-530-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced Polyethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.70 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 100 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 158 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 10800 | MPa | |
| 1000 hr | 8800 | MPa | |
| Flexural Modulus | 8950 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 10 | kJ/m² | |
| -30°C | 11 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 245 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 224 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | °C | ISO 306/B50 |
| Melting Temperature 1 | 252 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.0E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | 2.2E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | 4.0E-6 | cm/cm/°C | |
| Transverse | 8.1E-5 | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.7E-5 | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 38 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.60 | ASTM D150 | |
| 1 MHz | 3.50 | ASTM D150 | |
| 100 Hz | 4.20 | IEC 60250 | |
| 1 MHz | 3.90 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 5.0E-7 | ASTM D150 | |
| 1 MHz | 1.2E-6 | ASTM D150 | |
| 100 Hz | 0.013 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 38 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 20 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Neopor® F 5200 Plus | BASF Corporation | PS (EPS) | Neopor® |
| Amilan® CM3004-V0 | Toray Resin Company | Nylon 66 | Amilan® |
| CROSSVINIL EK/1 TPZ | Crosspolimeri S.p.A. | PVC, Unspecified | CROSSVINIL |
| Polimid B AV V0M | Poliblend S.p.a. | Nylon 6 | Polimid B |
| POTICON RF25X2 | Otsuka Chemical Co., Ltd. | PPS | POTICON |