Plexiglas® Satinice df33 zk6BR

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HAhOpC_Plexiglas-Satinice-df33-zk6BR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PLEXIGLAS® Satinice df33 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.

Typical properties of impact modified PLEXIGLAS® molding compound are

high break resistance and impact strength

improved resistance to stress cracking

good weather resistance

high surface hardness and mar resistance

the pleasant feel and sound of the moldings.

Extruded parts from PLEXIGLAS® Satinice df33 zk6BR are characterized by the following special properties:

excellent light diffusion combined with excellent light transmission

semi-gloss surfaces

touch and fingerprint resistant.

Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry, but also for injection molding items for lighting engineering applications.

Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.

General Information
Additive	Impact Modifier
Features	Good Surface Finish Good Weather Resistance High Clarity High Hardness High Impact Resistance High Scratch Resistance Impact Modified Medium Gloss Soft
Uses	Automotive Applications Construction Applications Furniture Lighting Diffusers Profiles Sheet
Appearance	Matte Finish
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.16	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	1.40	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2000	MPa	ISO 527-2/1
Tensile Stress (Yield)	45.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	4.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	25	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	40	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	99.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	96.0	°C	ISO 75-2/A
Vicat Softening Temperature	99.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	9.2E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	700	°C	IEC 60695-2-13

Optical	Nominal Value	Unit	Test Method
Transmittance ¹	67.0	%	ISO 13468-2

Additional Information	Nominal Value	Unit	Test Method
Half-Value Angle	36.0	°	DIN 5036
Scattering Power	0.490		DIN 5036

Extrusion	Nominal Value	Unit
Drying Temperature	< 85.0	°C
Drying Time	2.0 to 3.0	hr
Melt Temperature	230 to 260	°C
Die Temperature	230 to 260	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
TAROMID A 260 Y0	Taro Plast S.p.A.	Nylon 66/6	TAROMID A
TOTAL Polypropylene 3287WZ	TOTAL Refining & Chemicals	PP Homopolymer	TOTAL Polypropylene
Nipol® LX206	Zeon Corporation	Latex	Nipol®
AEI CT-1159:CM601	AEI Compounds Limited	XLPE	AEI
Cheng Yu ML1210	Cheng Yu Plastic Company Limited	PC	Cheng Yu