IROSTIC® S 8735

Category:	TPU, Unspecified , Thermoplastic Polyurethane Elastomer
Manufacturer:	Huntsman Corporation
Trademark:	IROSTIC®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HAb15T_IROSTIC-S-8735.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
IROSTIC® is the Huntsman trade name for a range of polyurethane based raw materials for the manufacture of TPU adhesives. IROSTIC® is globally available in a broad range of base polyol and isocyanate chemistries and can be used as a one or two-component system with IRODUR® cross-linkers. IROSTIC® "Footwear Adhesives" features: Very good heat resistance Good adhesion to various substrates Good green strength May be used as one or two component adhesives High tear resistance Good hydrolysis resistance Low temperature flexibility High peel strength IROSTIC® "Adhesives" applications: Footwear Laminating Adhesives Do It Yourself Textiles Print industry Bonding of woven / non-woven fabrics Athletic shoes and sporting goods Packaging materials Aerospace and automotive assemblies

Message

IROSTIC® is the Huntsman trade name for a range of polyurethane based raw materials for the manufacture of TPU adhesives.

IROSTIC® is globally available in a broad range of base polyol and isocyanate chemistries and can be used as a one or two-component system with IRODUR® cross-linkers.

IROSTIC® "Footwear Adhesives" features:

Very good heat resistance

Good adhesion to various substrates

Good green strength

May be used as one or two component adhesives

High tear resistance

Good hydrolysis resistance

Low temperature flexibility

High peel strength

IROSTIC® "Adhesives" applications:

Footwear

Laminating Adhesives

Do It Yourself

Textiles

Print industry

Bonding of woven / non-woven fabrics

Athletic shoes and sporting goods

Packaging materials

Aerospace and automotive assemblies

General Information
Uses	Adhesive

Physical	Nominal Value	Unit	Test Method
Viscosity- 15% solid in MEK ¹(20°C)	100 - 600	mPa·s

Additional Information	Nominal Value	Unit	Test Method
Crystallization Rate	11.0 - 15.0	min	Internal method
Flowability ²	88 - 165	°C	ASTM 28
Processing Temperature	130 - 150	°C
SAFT ³	56 - 160	°C	Internal method
Activation temperature	70 - 75	°C

Hardness	Nominal Value	Test Method
Durometer Hardness ⁴		DIN 53505
Shaw A	90 - 94	DIN 53505
Shaw D	43 - 45	DIN 53505

Elastomers	Nominal Value	Unit
Tensile Strength
Yield	7.00 - 8.00	MPa
Fracture	12.0 - 19.0	MPa
Tensile Elongation (Break)	900 - 1000	%

Additional Information	Nominal Value	Unit	Test Method
Excellent adhesion to: paper PVC wood textile leather

Note Message
1 .	# viscosities available within grade: 2
2 .	@ average viscosity
3 .	cotton-cotton 0.5 kg load
4 .	@ average viscosity

Resin Grade	Manufacturer	Category	Trademark
Sindustris PC GP2101	Sincerity Australia Pty Ltd.	PC	Sindustris PC
ADEKA EP-4000	Adeka Corporation	Epoxy	ADEKA
Fainplast PVC PG 58/K1-UV	Fainplast Compounds S.r.l	PVC+NBR	Fainplast PVC
Kumho EPS SEPS N16	Korea Kumho Petrochemical Co., Ltd.	PS (EPS)	Kumho EPS
NORYL GTX™ GTX975 resin	SABIC Innovative Plastics Europe	PPE+PS+Nylon	NORYL GTX™