GELOY™ XTWE480 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HAGtPu_GELOY-XTWE480-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anti-scratch GELOY grade with excellent weatherability, high flow, and good surface quality. XTWE480 is available in various colours. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 38 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness 1 | F | ASTM D3363 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2470 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 50.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break 4 | 36.0 | MPa | ASTM D638 |
| Break | 38.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Break 6 | 21 | % | ASTM D638 |
| Break | 25 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2060 | MPa | ASTM D790 |
| -- 8 | 2410 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 27 | J/m | ASTM D256 |
| 23°C | 49 | J/m | ASTM D256 |
| -30°C 10 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 6.50 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 73.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 78.0 | °C | ASTM D1525 13 |
| -- | 79.0 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.8E-5 | cm/cm/°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Cylinder Zone 1 Temp. | 205 to 220 | °C | |
| Cylinder Zone 2 Temp. | 210 to 225 | °C | |
| Cylinder Zone 3 Temp. | 215 to 225 | °C | |
| Cylinder Zone 4 Temp. | 215 to 225 | °C | |
| Adapter Temperature | 200 to 225 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Die Temperature | 210 to 225 | °C | |
| Calibration Temp, First | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1 kgf |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven F-651 | Propilven, S.A. | PP Random Copolymer | Propilven |
| Colorite 11 Series 9511 | Colorite Polymers | PVC, Unspecified | Colorite 11 Series |
| Geon™ HTX E1502 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| Jackdaw ABS GB11BK6589 | Jackdaw Polymers | ABS | Jackdaw ABS |
| LNP™ THERMOCOMP™ LF004E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |