Order Products : sales@su-jiao.com
Ultramid® 66 H2 G/35-V0KB NAT0046
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7vxem_Ultramid-66-H2-G-35-V0KB-NAT0046.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 66 H2 G/35-V0KB NAT0046 is a 35% glass reinforced, heat stabilized injection molding grade. It is a V-0 self-extinguishing grade, with phosphorous. It offers good flowability and mechanical properties. It has excellent electrical properties. Applications Ultramid 66H2 G/35-V0KB NAT0046 is designed for applications requiring good processing, mechanical integrity and flammability performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 247 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 285 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TC-C-55 | RTP Company | Nylon 66 | RTP |
| Tecnoflon® PL 455 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| BJB Polyurethane TC-962 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Hylac® GP55G10 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| POCAN® T 7323 000000 | LANXESS GmbH | PBT+PET | POCAN® |