LNP™ STAT-KON™ RFD04 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7mcqh_LNP-STAT-KON-RFD04-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound RF-20 Product reorder name: RFD04 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.39 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 3.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.4 | % | ISO 294-4 |
| Flow : 24 hr | 0.61 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.50 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.75 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9200 | MPa | ASTM D638 |
| -- | 8780 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 124 | MPa | ASTM D638 |
| Break | 117 | MPa | ISO 527-2 |
| Break | 119 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 8540 | MPa | ASTM D790 |
| -- | 8600 | MPa | ISO 178 |
| -- 5 | 8180 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 185 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 36 | J/m | ASTM D256 |
| 23°C 7 | 3.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D4812 |
| 23°C 8 | 20 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.60 | J | ASTM D3763 |
| -- | 1.46 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 257 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 248 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 242 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -30 to 30°C | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Flow : -40 to 40°C | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -30 to 30°C | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Transverse : -40 to 40°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*3 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP44-10MG | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Sindustris PP R7701 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| SynPlast™ NOTM-E | PolyOne Corporation | Tri (n-octyl) Trimellitate | SynPlast™ |
| TRANSMARE® 19HGF40-1.003 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Kingfa FRHIPS-100 | Kingfa | PS (HIPS) | Kingfa |