Telcar® TL-8712R
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7WhTz_Telcar-TL-8712R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar TL-8712R is a flame retardant thermoplastic elastomer designed for electrical applications requiring flexibility over a wide termperture range. Telcar TL-8712R is a medium durometer grade that is RoHS compliant. This grade is suitable for both injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 71 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 0.508mm 2 | 2.48 | MPa | ASTM D412 |
| 300% strain, 0.508mm 3 | 3.65 | MPa | ASTM D412 |
| Tensile Strength (fracture, 0.508mm) | 13.8 | MPa | ASTM D412 |
| Tensile Elongation (fracture, 0.508mm) | 680 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (136°C, 168 hr) | 9.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (136°C, 168 hr) | -1.0 | % | ASTM D573 |
| Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil) | -8.0 | % | ASTM D471 |
| Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil) | 3.0 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 105 | °C | ASTM D794 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (50°C) | 6.6E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 2.10 | ASTM D150 | |
| 1 MHz | 2.10 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | die cut from extruded tapes |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 GF 30 FRG 5 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| TIPPLEN® R 780 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| Topolymer® 8210-T | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| GAPEX® HP RPP30EC16BK | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| ESTOPLAST EP 5510GY02 | Ester Industries Ltd. | PBT | ESTOPLAST EP |