Sindustris ABS LTR662
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H7QRd5_Sindustris-ABS-LTR662.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LTR662 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LTR662 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 | |
| Pencil Hardness | 1H | ASTM D3363 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2750 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 57.9 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm | 6.0 | % | |
| Break, 3.20 mm | 37 | % | |
| Flexural Modulus 4(6.40 mm) | 2650 | MPa | ASTM D790 |
| Flexural Strength 5(6.40 mm) | 92.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | |
| -30°C, 6.40 mm | 59 | J/m | |
| 23°C, 3.20 mm | 120 | J/m | |
| 23°C, 6.40 mm | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 92.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 91.0 | % | ASTM D1003 |
| Haze | 1.5 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 240 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Capran® UNIDRAW 104 | Honeywell | Nylon 6 | Capran® |
| Electrafil® J-1305/CF/30/TF/15 NAT | Techmer Engineered Solutions | PPS | Electrafil® |
| Kingfa API-1508 | Kingfa | PP, Unspecified | Kingfa |
| Karina CLEAR PVC COMPOUND 80/218-IS-RG-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TechnoFiber PP LGF 60-10-01 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |