SLOVAMID® 66 HI/1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H6VF7a_SLOVAMID-66-HI-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safety use /hockey, building/, protection frames of cardoors. Withstands high dynamic stress up to - 40°C. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 2.8 | % | |
| Flow | 3.5 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2230 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 28 | % | ISO 527-2 |
| Flexural Modulus | 2070 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 10 | kJ/m² | |
| 23°C | 44 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 59.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 190 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 2200 | POLY GIN | PC | MARCOBLEND |
| Trilene FreeFlow™ CP5000 | Lion Copolymer, LLC | EPM | Trilene FreeFlow™ |
| Adell PC YS-10 | Adell Plastics, Inc. | PC Alloy | Adell PC |
| Diaterm® A27 GF30TF10 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |
| Petrotene® PP A3 T40 NTLA010 PH320 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |