HAIPLEN H50 Y0
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H5u5Gi_HAIPLEN-H50-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer self extinguishing V0 halogen free, good flow and mechanical properties. UL94 V0 - all colors - 1,6 mm Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 | % | |
| Across Flow | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 130 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 4 2 |
| -- | 95.0 | °C | ASTM D1525, ISO 306/B 5 3 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (1.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 20000 hrs |
| 2 . | Loading 1 (10 N) |
| 3 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STERalloy™ FDG 2791 | Hapco Inc. | TP, Unspecified | STERalloy™ FDG |
| SUPREME Specialty PS SP263 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Badamid® LA70 GF50 HH | Bada AG | Nylon 66 | Badamid® |
| Cri-Line FDA-615-65-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Karina CLEAR PVC COMPOUND 78/200-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |