NOVALAC RX®611V Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
NOVALAC RX®611V is a phenolic (Phenolic) material, and its filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. NOVALAC RX®The main features of 611V are: chemical resistance high strength Creep resistance Good dimensional stability Good toughness Typical application areas include: Electrical/electronic applications engineering/industrial accessories electrical appliances House Tools

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Ultra high toughness Good dimensional stability Low smoke High strength Antibacterial property Solvent resistance Good creep resistance alkali resistance acid resistance
Uses	Membrane key switch Pump parts Gear Electrical/Electronic Applications Electrical appliances Power/other tools Connector Application in Automobile Field Shell
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.67	g/cm³	ISO 1183
Molding Shrinkage - Flow	0.15	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.070	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (E-Scale)	95		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	115	MPa	ISO 527-2
Flexural Modulus	16000	MPa	ISO 178
Flexural Stress	130	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	2.5	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	195	°C	ISO 75-2/A
CLTE - Flow	1.2E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.47	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	10	kV/mm	IEC 60243-1
Arc Resistance	125	sec	ASTM D495

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Back Pressure	0.207	MPa

Injection instructions
Plastication: 50rpmInjection Pressure: Set to give 3 to 5 seconds injection timeHold Pressure: 50 to 100% of injection pressureHold Time: 10 sec minimumCure Time, 0.125 in: 30 to 35 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens.Compressive Strength, ISO 604: 320 MPaDielectric Strength, IEC 243, Method A, wet: 10 V/milCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Injection instructions

Plastication: 50rpmInjection Pressure: Set to give 3 to 5 seconds injection timeHold Pressure: 50 to 100% of injection pressureHold Time: 10 sec minimumCure Time, 0.125 in: 30 to 35 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens.Compressive Strength, ISO 604: 320 MPaDielectric Strength, IEC 243, Method A, wet: 10 V/milCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	NOVALAC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	H4VzVc_NOVALAC-RX-611V.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TPX® RT18	Mitsui Chemicals America, Inc.	PMP Copolymer	TPX®
Ferro PP TPP40AE64GY	Ferro Corporation	PP Homopolymer	Ferro PP
Hyrene® PS-MI 14/1.3	Entec Polymers	PS (MIPS)	Hyrene®
Karina WHITE PVC COMPOUND 800D10/7-A-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 8260-85 Brown 7487	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin