SABIC® PPcompound 8620
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H4MVbM_SABIC-PPcompound-8620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was originally designed for painted or unpainted automotive bumper fascia applications where a combination of high stiffness and cold temperature ductility is required. The IMDS is 209747700. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C, 1 hr | 0.80 | % | |
| Across Flow : 120°C, 30 min | 0.90 | % | |
| Across Flow : 23°C, 48 hr | 0.70 | % | |
| Flow : 80°C, 1 hr | 0.50 | % | |
| Flow : 120°C, 30 min | 0.60 | % | |
| Flow : 23°C, 48 hr | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 54 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1680 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 17.0 | MPa | ASTM D638 |
| Yield | 17.0 | MPa | ISO 527-2/50 |
| Break 3 | 12.0 | MPa | ASTM D638 |
| Break | 11.5 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 39 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1390 | MPa | ASTM D790 |
| 64.0 mm Span 7 | 1740 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 7.0 | kJ/m² | |
| 0°C 9 | 26 | kJ/m² | |
| 23°C 10 | 58 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 11 | 540 | J/m | ASTM D256 |
| -30°C 12 | 6.9 | kJ/m² | ISO 180/1A |
| 0°C 13 | 26 | kJ/m² | ISO 180/1A |
| 23°C 14 | 50 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 15(23°C, 3.20 mm) | No Break | ASTM D4812 | |
| Instrumented Dart Impact 16 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 21.6 | J | |
| 0°C, Energy at Peak Load | 17.7 | J | |
| 23°C, Energy at Peak Load | 16.3 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 98.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 17 | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 52.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 18 | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 123 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 41.2 | µm/Mk | |
| Transverse : -30 to 100°C | 167 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 80*10*4 mm, Cut |
| 11 . | 63.5*12.7*3.2mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 80*10*4mm, Cut |
| 14 . | 80*10*4mm, Cut |
| 15 . | 63.5*12.7*3.2mm, Cut |
| 16 . | 2.20 m/sec |
| 17 . | 80*10*4mm, Cut |
| 18 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santron IMS2000 | Bhansali Engineering Polymers Limited | SAN | Santron |
| INSUL-PLATE™ X-28057-2HT | Sumitomo Bakelite North America, Inc. | Epoxy | INSUL-PLATE™ |
| Arnite® TV4 240 S | DSM Engineering Plastics | PBT | Arnite® |
| Eraclene® FB 506 | Versalis S.p.A. | HDPE | Eraclene® |
| Iupital® TC3015 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |