| PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 35 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 11.2 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 1.0 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.10 | % | |
| Equilibrium, 23°C, 50% RH | 0.030 | % | |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 48.0 | MPa | Internal Method |
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/50 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Break | 250 | % | Internal Method |
| Break 5 | 50 | % | ASTM D638 |
| Break | 42 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2200 | MPa | ASTM D790 |
| -- 7 | 2130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 73.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 52 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 10 | 8.4 | kJ/m² | ISO 180/1A |
| 23°C 11 | 41 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Total Energy | 50.0 | J | |
| 23°C, Total Energy | 50.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 119 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 77.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525 13 |
| -- | 122 | °C | ISO 306/B50 |
| -- | 124 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | ||
| 125°C | Pass | ||
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 3.00 mm 14 | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | |
| 3.00 mm | 725 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| 14 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP673-01 | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Sindustris PP H7501 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Witcom PC EC-EM-FR | Witcom Engineering Plastics B.V. | PC | Witcom PC |
| Kemcor HD 0811 | Qenos Pty Ltd | HDPE, HMW | Kemcor |
| Kepital® ES-20 | KEP Americas | Acetal (POM) Copolymer | Kepital® |