AKROMID® A3 ICF 15 black (5056)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H4Fa2A_AKROMID-A3-ICF-15-black-5056-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 ICF 15 black (5056) is a 15% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.20 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 50.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.40 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 7400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 170 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10400 | 7000 | MPa | ISO 178 |
| Flexural Stress 2 | 250 | 170 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 3.0 | 5.0 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 15 | -- | % | ISO 1172 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 45 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+5 | 1.0E+5 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001 | PolyOne Corporation | PC | Stat-Tech™ |
| Axplas® MEP52 0074 | Axion Polymers | TP, Unspecified | Axplas® |
| EcoLon® MRGF1518-BK3 | Wellman Engineering Resins | Nylon 66 | EcoLon® |
| Karina PVC COMPOUND WHITE COLOR - E-800-10/1-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® V920-UVT | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |