AKROMID® T1 GF 30 black (3466)
| Category: | PPA , Polyphthalamide |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H3gbRZ_AKROMID-T1-GF-30-black-3466-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® T1 GF 30 black (3466) is a 30% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance Applications are parts with tight dimensional tolerances even under high mechanical load. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.40 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 73.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.3 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 3.0 | -- | % | ISO 178 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 150 to 160 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 170 to 180 | -- | °C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 290 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 215 | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.2 | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 11000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | -- | kJ/m² | |
| 23°C | 60 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 310 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 165 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 313 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1-5005F | Spartech Polycom | ABS | Spartech |
| Yanshan PE LD358 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Nypol® PA B3 G10 BRC0003 NT386 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Borealis PP BD212CF | Borealis AG | PP Copolymer | Borealis PP |
| Gazprom 15803-020 (Prime Grade) | JSC Gazprom neftekhim Salavat | LDPE | Gazprom |