Latigray 88/10-01 CX/30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigray |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H3a3OD_Latigray-88-10-01-CX-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Radiopaque compound based on Polyetheretherketone (PEEK). Special filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.3 | % | |
| Flow : 2.00 mm | 0.80 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 75.0 | MPa | |
| Break, 23°C | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.3 | % | |
| Break, 23°C | 10 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3(23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4(23°C) | 70 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 170 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 300 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 to 170 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 380 to 400 | °C | |
| Mold Temperature | 180 to 190 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 80x10x4 mm |
| 3 . | 80x10x4 mm |
| 4 . | 63.5x12.7x3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 524M | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| TYNEA 3130 | Tyne Plastics LLC. | Acetal (POM) Homopolymer | TYNEA |
| Generic Silicone - Carbon Fiber | Generic | Silicone | Generic |
| Electrafil® PA6/6 05012 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| MARPOL® F-S | Marco Polo International, Inc. | PS (EPS) | MARPOL® |