CABELEC® CA4701
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H2yBXe_CABELEC-CA4701.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 4701 is an electrically conductive compound based on carbon black and a polypropylene copolymer. Its electrical and mechanical properties are permanent and are not dependent on atmospheric conditions. CABELEC® 4701 has been specially designed for sensitive extrusion applications such as sheets and corrugated sheets for packaging electronics, where freedom from the hazard of electrostatic discharge is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.21 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 230°C/10.0 kg | 10 | g/10 min | |
| 230°C/5.0 kg | 2.3 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 3(Shore D, 15 sec) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | ISO 527-2 | ||
| Yield | 27.5 | MPa | |
| Break | 19.5 | MPa | |
| Tensile Strain 5(Break) | 37 | % | ISO 527-2 |
| Flexural Modulus 6 | 1110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 7(23°C) | 72 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 9 | 155 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 10 | 9.8E+2 | ohms | |
| 0.400 mm 11 | 7.7E+2 | ohms | |
| Volume Resistivity 12 | 70 | ohms·cm | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E030 |
| 4 . | CTM E041 |
| 5 . | CTM E041 |
| 6 . | CTM E040A |
| 7 . | CTM E044A |
| 8 . | CTM E038 |
| 9 . | CTM E039 |
| 10 . | CTM E042E |
| 11 . | CTM E042D |
| 12 . | CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P VH | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Sinvicomp SRF3709Z | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Titanvene™ HD6070EA | PT. TITAN Petrokimia Nusantara | HDPE | Titanvene™ |
| APEX® RM 8201 | Teknor Apex Company | PVC, Rigid | APEX® |
| LUVOCOM® PEEK CLASSIX 7918 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |