Boda BDT246-2CP
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H2p3s0_Boda-BDT246-2CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDT246-2CP is a medium to high viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good processing properties and superior fluid resistance than standard terpolymers are required. BDT246-2CP can be compounded to meet the major fluoroelastomer specifications. BDT246-2CP can be used for compression molding of O-rings and gaskets. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 46 | MU | |
| Fluorine Content | 69 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.30 | N·m | |
| ML 2(177°C) | 0.240 | N·m | |
| t'90 3(177°C) | 2.7 | min | |
| ts2 4(177°C) | 1.3 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.8 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 230 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 26 | % | ASTM D395B |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (23°C, 168 hr, Class C Standard Fuel) | -30 | % | ASTM D471 |
| Change in Ultimate Elongation (23°C, 168 hr, Class C Standard Fuel) | -4.0 | % | ASTM D471 |
| Change in Durometer Hardness (23°C, 168 hr, in Reference Fuel C) | -15 | ASTM D471 | |
| Change in Volume (23°C, 168 hr, Class C Standard Fuel) | 20 | % | ASTM D471 |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarTUFF TF 75-LR-1 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| NEFTEKHIM PP 2641J (T31SE) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Mylar® EL-21 (1000 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| DuPont™ 20 Series DPE-2010 | DuPont Packaging & Industrial Polymers | LDPE | DuPont™ 20 Series |
| Karina RED PVC COMPOUND 830-42/16-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |