SCHULAMID® B 6 MKF 4015
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H2CobS_SCHULAMID-B-6-MKF-4015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% glassfiber and mineral reinforced polyamide 6 compound with high mechanical strength and dimensional stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.44 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7800 | 4200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | 65.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | 10 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.6 | -- | kJ/m² | |
| 23°C | 4.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | -- | kJ/m² | |
| 23°C | 45 | 60 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 192 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 220 | -- | °C | ISO 306/A50 |
| -- | 215 | -- | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS 1002 | ROMIRA GmbH | ABS | Rotec® ABS |
| Strator® B-6 | EPIC Polymers | Nylon 6 | Strator® |
| Ultramid® B36 | BASF Corporation | Nylon 6 | Ultramid® |
| Fainplast PVC PG 80 | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Karina MBU BLUEL -E 06/923-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |