ULTEM™ SF2255 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H26caD_ULTEM-SF2255-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High flow Ultem for thin wall application |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (345°C/10.0 kg) | 34.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.30 | % | |
| Across Flow | 0.53 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10100 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 148 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.8 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 8090 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 169 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 76 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 203 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 150°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -40 to 150°C | 5.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CYCOLOY™ RCX7233 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| KumhoSunny PC/ABS HAC8265 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina CLEAR CRYSTAL PVC COMPOUND -E 70/200-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-9051/LGF/BK | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 2900-45 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |