RTP ESD C 260H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H24vH1_RTP-ESD-C-260H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 - 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 51.7 | MPa | ASTM D638 |
| -- | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 18 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 124 | MPa | ASTM D790 |
| Yield | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 270 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.7 | °C | ASTM D648 |
| CLTE - Flow | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 18-22mil/in.Tensile Elongation, ASTM D638: 15-20%NFPA Code 56A, static decay rate, 0.5 sec: passes |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 260 - 288 | °C | |
| Middle Temperature | 260 - 288 | °C | |
| Front Temperature | 260 - 288 | °C | |
| Mold Temperature | 79.4 - 121 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 403 HI | RTP Company | PS (HIPS) | RTP |
| ALTECH® PA66 C 1000/506 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Aplax P2220GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| LEXAN™ HFR1724 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| POCAN® ECO T 3230 000000 | LANXESS Corporation | PBT+PET | POCAN® |