VALOX™ 420 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H1oUHH_VALOX420resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 420 is a 30% glass fiber reinforced PBT injection moulding resin with excellent mechanical and thermal properties. Applications: appliance handles, spotlights, electric motors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 55 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 12.0 | cm³/10min | ISO 1133 |
| 250°C/5.0 kg | 30.0 | cm³/10min | ISO 1133 |
| 265°C/5.0 kg | 45.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Flow | 0.30 - 0.70 | % | Internal method |
| Transverse flow | 0.50 - 1.0 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.26 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 125 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 10300 | MPa | ASTM D638 |
| -- | 10300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 145 | MPa | ASTM D638 |
| Yield | 135 | MPa | ISO 527-2/5 |
| Fracture 4 | 145 | MPa | ASTM D638 |
| Fracture | 135 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 6 | 3.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 8000 | MPa | ASTM D790 |
| -- 8 | 8500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 205 | MPa | ISO 178 |
| -- | 200 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 190 | MPa | ASTM D790 |
| Fracture, 50.0mm span 10 | 190 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 19.0 | mg | Internal method |
| Flexural Strain at Break 11 | 4.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 30 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 12 | 5.0 | kJ/m² | ISO 179/1eA |
| -30°C | 11 | kJ/m² | ISO 179/2C |
| 23°C 13 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -30°C 14 | 45 | kJ/m² | ISO 179/1eU |
| -30°C | 50 | kJ/m² | ISO 179/2U |
| 23°C 15 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 0°C | 110 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -40°C 16 | 5.0 | kJ/m² | ISO 180/1A |
| -30°C 17 | 9.0 | kJ/m² | ISO 180/1A |
| 0°C 18 | 10 | kJ/m² | ISO 180/1A |
| 23°C 19 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 970 | J/m | ASTM D4812 |
| 23°C | 970 | J/m | ASTM D4812 |
| -30°C 20 | 45 | kJ/m² | ISO 180/1U |
| 23°C 21 | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 220 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 22 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 205 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 23 | 205 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ASTM D1525 24 |
| -- | 220 | °C | ASTM D1525, ISO 306/A50 15 25 |
| -- | 215 | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 1.8E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.19 | W/m/K | ISO 8302 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 0.800 mm, in Oil | 30 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 24 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 16 | kV/mm | ASTM D149 |
| 0.800mm, in oil | 30 | kV/mm | IEC 60243-1 |
| 1.00 mm 26 | 19 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 24 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.10 | IEC 60250 | |
| 60 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Arc Resistance 27 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.840 mm | HB | UL 94 | |
| 6.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 825 | °C | IEC 60695-2-13 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 130 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 80*10*4 |
| 22 . | 80*10*4 mm |
| 23 . | 80*10*4 mm |
| 24 . | 标准 B (120°C/h), 载荷2 (50N) |
| 25 . | 速率 A (50°C/h), 载荷2 (50N) |
| 26 . | Short-Time |
| 27 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SANREX SAN-L | Techno Polymer Co, Ltd. | SAN | SANREX |
| Tecomid® NB40 GR15 NL HS | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| KER® 1502 | Synthos S.A. | SBR, Emulsion | KER® |
| LNP™ THERMOCOMP™ PF003 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| HIFOR® LF1030AA | Westlake Chemical Corporation | LLDPE | HIFOR® |