Karina BLACK PVC COMP. 809D48/ 1-C-AC-AS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H1kz3T_Karina-BLACK-PVC-COMP-809D48-1-C-AC-AS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE / FLAME-RETARDANT AND HIGH SOLIDITY TO LIGHTNESS / RECOMMENDED FOR EXTRUSION OF COAXIAL COATING AND ALSO FOR FLEXIBLE AUTOMOTIVE TUBES WORKING FROM -40C UNTIL +80C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.33 to 1.39 | g/cm³ | IEC 60811-1-3 |
| Color | OK | ME 12 | |
| Color a | -0.750 to 0.850 | ME 12 | |
| Color b | -0.970 to 0.630 | ME 12 | |
| Color L | 25.5 to 27.1 | ME 12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | NBR 5403 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 28 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 TFE 15 | RTP Company | PBT | RTP |
| SEPAZ™ LC50 | Mando Advanced Materials Co., Ltd. | PP Copolymer | SEPAZ™ |
| AKROMID® A3 GF 50 1 blue (3778) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| LNP™ KONDUIT™ PX10323 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ KONDUIT™ |
| PALMID® R 6 E | pal plast GmbH | Nylon 6 | PALMID® |