LUBEMID A26 TF10 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | H0Q97Z_LUBEMID-A26-TF10-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA66 natural first choice. Self lubricated. With PTFE. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 to 1.21 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 to 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 60.0 to 70.0 | MPa | |
| Break | 60.0 to 70.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 5.0 to 7.0 | % | |
| Break | 5.0 to 7.0 | % | |
| Flexural Modulus 1 | 2300 to 2700 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 to 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 to 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 to 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 30 to 45 | J/m | ASTM D256A |
| 23°C 3 | 45 to 55 | kJ/m² | ASTM D256 |
| 23°C | 3.0 to 3.5 | kJ/m² | ISO 180/A |
| 23°C 4 | 3.0 to 4.5 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 45 to 55 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 to 230 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 220 to 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 to 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 245 to 255 | °C | ISO 306/A120 |
| -- | 225 to 235 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC0LEZ (Series: UV/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Bergamid™ A700 G50 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Evolue™ SP2320H | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Gallonprene® GP520-7509 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hapflex™ 560 | Hapco Inc. | TP, Unspecified | Hapflex™ |