Moplen HP552K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzxsAi_Moplen-HP552K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen HP552K is used in extrusion applications. It is formulated with an anti-gasfading stabilisation package. Moplen HP552K is used in the production of high tenacity staple fibres. Typical application is nonwovens. For regulatory information please refer to Moplen HP552K Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 34.0 | MPa | |
| Break | 23.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | > 500 | % | |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 220 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 93.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3705ZE | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Xuchuan A-9007/B-6088 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Keyflex® TO 1088AV | LG Chem Ltd. | TPC-ET | Keyflex® TO |
| HiFill® PA6/6 GB25 L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Leona™ 1702 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |