Latigloss 66 H2 K/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigloss |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gzl3No_Latigloss-66-H2-K-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Heat stabilised. Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 to 0.85 | % | |
| Flow : 2.00 mm | 0.15 to 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 21000 | MPa | |
| 60°C | 16000 | MPa | |
| 90°C | 10000 | MPa | |
| 120°C | 6100 | MPa | |
| 150°C | 4900 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 230 | MPa | |
| Break, 60°C | 155 | MPa | |
| Break, 90°C | 110 | MPa | |
| Break, 120°C | 80.0 | MPa | |
| Break, 150°C | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.7 | % | |
| Break, 60°C | 2.6 | % | |
| Break, 90°C | 4.2 | % | |
| Break, 120°C | 4.6 | % | |
| Break, 150°C | 5.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 245 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STATEX® 31 | ITW FORMEX | PP, Unspecified | STATEX® |
| TAROLON 3000 Y0 | Taro Plast S.p.A. | PC | TAROLON |
| Xuchuan XCY-5533A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Novalloy-B B1500, B1500F | Daicel Polymer Ltd. | ABS+PBT | Novalloy-B |
| Braskem PP TI4700P2 | Braskem America Inc. | PP Impact Copolymer | Braskem PP |