Comco PETP - GL
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Comco-Plastic GmbH |
| Trademark: | Comco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gzd89Y_Comco-PETP---GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Comco PETP - GL is a Polyethylene Terephthalate (PET) material. It is available in Europe. Primary attribute of Comco PETP - GL: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption | |||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ISO 2039-2 | |
| Ball Indentation Hardness | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 76.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | > 15 | % | ISO 527-2 |
| Tensile Creep Modulus 1(1000 hr) | 23.0 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604 | ||
| 5% Strain | 95.0 | MPa | |
| 2% Strain | 47.0 | MPa | |
| 1% Strain | 24.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | > 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 2.5 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 340 | °C | |
| Thermal Conductivity | 0.24 | W/m/K | |
| Maximum Service Temperature | |||
| in air continuosly | 115 | °C | |
| in air for short periods | 160 | °C | |
| Service Temperature - Minimum | -20 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 21 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 0.014 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | 1% Strain |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 45A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| WELLAMID Nylon 6000/52 GV 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Durethan® BKV 115 H3.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Dapol® D2200F | Fudow Co., Ltd. | DAP | Dapol® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8271 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |