Generic PESU - Glass Fiber
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzTh0G_Generic-PESU---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PESU - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.44 - 1.68 | g/cm³ | ASTM D792 |
| 23°C | 1.45 - 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.60 | % | ASTM D955 |
| Transverse flow : 23°C | 0.40 - 0.71 | % | ASTM D955 |
| 23°C | 0.19 - 0.72 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.30 - 0.41 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.49 - 0.75 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 120 - 134 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4360 - 12500 | MPa | ASTM D638 |
| 23°C | 4420 - 11100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 96.5 - 111 | MPa | ASTM D638 |
| Yield, 23°C | 102 - 146 | MPa | ISO 527-2 |
| Fracture, 23°C | 101 - 152 | MPa | ASTM D638 |
| Fracture, 23°C | 87.0 - 146 | MPa | ISO 527-2 |
| 23°C | 95.0 - 161 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.9 - 4.1 | % | ASTM D638 |
| Yield, 23°C | 1.2 - 4.3 | % | ISO 527-2 |
| Fracture, 23°C | 1.4 - 3.8 | % | ASTM D638 |
| Fracture, 23°C | 1.3 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4130 - 11800 | MPa | ASTM D790 |
| 23°C | 3930 - 10900 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 152 - 224 | MPa | ASTM D790 |
| 23°C | 137 - 222 | MPa | ISO 178 |
| Compressive Strength (23°C) | 109 - 152 | MPa | ASTM D695 |
| Coefficient of Friction | 0.15 - 0.46 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.9 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 - 48 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 48 - 98 | J/m | ASTM D256 |
| 23°C | 5.0 - 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 360 - 760 | J/m | ASTM D256 |
| 23°C | 29 - 73 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 6.98 - 16.0 | J | ASTM D3763 |
| 23°C | 2.47 - 4.49 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 207 - 221 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 214 - 224 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 204 - 216 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 - 219 | °C | ISO 75-2/A |
| Continuous Use Temperature | 180 | °C | ASTM D794 |
| Vicat Softening Temperature | 215 - 220 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 4.0E-6 - 4.4E-5 | cm/cm/°C | ASTM D696 |
| Flow | 5.4E-6 - 4.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.3E-5 - 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.9E-5 - 4.8E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 2.8E-5 - 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.29 - 0.32 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 8.0 - 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 2.0E+2 - 1.3E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 15 - 18 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.70 - 4.30 | ASTM D150 | |
| Dissipation Factor (23°C) | 6.8E-3 - 7.0E-3 | ASTM D150 | |
| Arc Resistance | 70.0 - 150 | sec | ASTM D495 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.050 | % | |
| Rear Temperature | 348 - 371 | °C | |
| Middle Temperature | 360 - 371 | °C | |
| Front Temperature | 359 - 377 | °C | |
| Nozzle Temperature | 350 - 360 | °C | |
| Processing (Melt) Temp | 349 - 371 | °C | |
| Mold Temperature | 134 - 160 | °C | |
| Injection Pressure | 85.5 - 88.8 | MPa | |
| Back Pressure | 0.500 - 0.671 | MPa | |
| Screw Speed | 74 - 80 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PESU - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP263 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Clariant Nylon 6/6 PA-113CF30 TF15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Colorite G Series 7512G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Geon™ Vinyl Flexible B6000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Innothane® IE-3066 | Innovative Polymers, Inc. | TSU | Innothane® |