EPO-TEK® H20E-SLR-HV
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzOegT_EPO-TEK-H20E-SLR-HV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® H20E-SLR-HV is a two-component, electrically conductive, epoxy adhesive designed for solar ribbon bonding of photovoltaic modules. It provides the electrical back-contact for ribbon stringing of solar cells into modules and panels. It is a higher viscosity version of EPO-TEK H20E-SLR. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 400 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 6.11 | GPa | |
| Thixotropic Index | 3.51 | ||
| Weight Loss on Heating | |||
| 200°C | 0.36 | % | |
| 250°C | 1.3 | % | |
| 300°C | 2.4 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | 84.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.1E-5 | cm/cm/°C | |
| -- 3 | 2.6E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.5 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 7.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Silver | ||
| -- 5 | Silver | ||
| Density | |||
| Part A | 1.96 | g/cm³ | |
| Part B | 3.19 | g/cm³ | |
| Viscosity 6(23°C) | 7.0 | Pa·s | |
| Curing Time (140°C) | 0.17 | hr | |
| Pot Life | 1100 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 | ||
| Lap Shear Strength (23°C) | 12.7 | MPa | |
| Volume Resistivity (23°C) | < 4.0E-3 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN602G30 | RJM International, Inc. | Nylon 66 | RJM |
| ACCUTECH™ CP0437C20L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Evoprene™ HP 3722 | AlphaGary | SBC | Evoprene™ HP |
| Durethan® BM 29 X H2.0 EF 900116 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| SECCO S1003 | Shanghai SECCO Petrochemical Co., Ltd | PP Homopolymer | SECCO |