Plexiglas® Hi-Gloss NTA-1
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzBEiO_Plexiglas-Hi-Gloss-NTA-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Profile: PLEXIGLAS® Hi-Gloss NTA-1 is an impact-modified compound with a high heat deflection temperature based on polymethyl methacrylate (PMMA). Besides the well-known properties of PLEXIGLAS® molding compound, such as
PLEXIGLAS® Hi-Gloss NTA-1 offers the added benefits of
Application: PLEXIGLAS® Hi-Gloss NTA-1 is particularly suitable for injection molding technical components. Owing to its superior brilliance, high-gloss (Class A) surfaces can be obtained in opaque colors. Examples: add-on automotive body parts, mirror housings, pillar panels, spoilers Processing: PLEXIGLAS® Hi-Gloss NTA-1can be processed on machines with 3-zone general purpose screws for engineering thermoplastics. Physical Form / Packaging: PLEXIGLAS® Hi-Gloss NTA-1 compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags or in 500kg boxes with PE lining; other packaging on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 3.00 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | > 3.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 68.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 10 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 33 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| Glass Transition Temperature | 120 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 110 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 675 | °C | IEC 60695-2-13 |
| Fire Rating | B2 | DIN 4102 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 85.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOLEN R250 IM | SIBUR, LLC | PP Random Copolymer | TOLEN |
| Alathon® M5370WC | LyondellBasell Industries | HDPE Copolymer | Alathon® |
| APEX® 4168 | Teknor Apex Company | PVC, Flexible | APEX® |
| Braskem PP C7057-07 (Injection Molding) | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| Softell TKG 300N 1 C12871 | LyondellBasell Industries | PP Copolymer | Softell |