ACCUTECH™ CP0437W20L1
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzAGio_ACCUTECH-CP0437W20L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0437W20L1 is a polypropylene copolymer (PP Copoly) product, which contains a filler of 20% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 17.0 | MPa | ASTM D638 |
| Fracture | 14.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 25 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Flexural Strength | 20.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 86.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 53.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4301R45H | Technical Polymers, LLC | PPA | Thermec™ |
| Grilamid® L 25 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Hostaform® CP15X | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| INEOS PP H03W-01 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Sumikon® PM-3025 | SBHPP | Phenolic | Sumikon® |