Westlake MDPE EB171
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake MDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GzA5Si_Westlake-MDPE-EB171.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Westlake EB171 is a MDPE resin suggested for use in shrink packaging applications. This material has good TD shrinkage, good optical properties, excellent machinability and toughness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 33 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 33 µm, Blown Film | 338 | MPa | |
| 1% Secant, TD : 33 µm, Blown Film | 448 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 33 µm, Blown Film | 26.2 | MPa | |
| TD : Break, 33 µm, Blown Film | 18.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 33 µm, Blown Film | 300 | % | |
| TD : Break, 25 µm, Blown Film | 800 | % | |
| Dart Drop Impact (33 µm, Blown Film) | < 65 | g | ASTM D1709 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WEVO-CHEMIE Polyurethanes PU 403 FL/300 RE | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| ASTALAC™ ABS DMT | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| LNP™ THERMOCOMP™ RX10408H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| MAJORIS G600 | AD majoris | PP, Unspecified | MAJORIS |
| Petro Rabigh PP AZ564G | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |