Edistir® N 3560
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gz5YoZ_EdistirN3560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High molecular weight general purpose polystyrene with good mechanical strength and good thermal resistance. N 3560 belongs to Edistir® GPPS third generation. It is recommended for in line forming of disposable packaging, for sheet extrusion in blend with conventional or clear high impact PS and for injection moulding of complex items requiring good toughness and improved elasticity. Thanks to N 3560, injected items will be more brilliant and neutral coloured, in line with more sophisticated market needs. Designation: Thermoplastics ISO 1622-PS,G,095-03. Applications Suitable for thermoformed food packaging articles as drink and dairy cups, plates trays and for injection moulded cd boxes, internal fridge items, domestic appliances, stationery, cutlery, housewares. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.8 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Stress 1 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 1.6 | kJ/m² | ISO 180/1A |
| 12°C | 1.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 2(1.8 MPa, Annealed) | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/A50 |
| -- | 91.0 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | IEC 60243-1 |
| Relative Permittivity (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 2.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm, ALL) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.6 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastics ISO 1622-PS,G,095-03 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 260 | °C | |
| Mold Temperature | 10 - 50 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW1988 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Viprene™ P80A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Trexprene® A80BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Unichem 8512B-02 | Colorite Polymers | PVC, Flexible | Unichem |
| DENIFORM 2510 | Vamp Tech | Acetal (POM) Copolymer | DENIFORM |