Order Products : sales@su-jiao.com
TOLEN H018 BM
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SIBUR, LLC |
| Trademark: | TOLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GyVRN8_TOLEN-H018-BM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP H018 BM is a polypropylene homopolymer with standard molecular mass distribution. The product features lower than average fluidity and a special stabilizing package containing a complex of additives that ensure necessary physical, mechanical properties and application performance of final products. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.8 | g/10 min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 30.0 | MPa | Internal Method |
| Tensile Strain 2(Yield) | 10 | % | Internal Method |
| Flexural Modulus 3 | 1550 | MPa | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | Internal Method |
| Vicat Softening Temperature | 155 | °C | Internal Method 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | A (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 862 | RTP Company | Acetal (POM) Homopolymer | RTP |
| Tecomid® NA30 NL RM | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| NORYL GTX™ GTX673 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| LNP™ STAT-KON™ EX99689C compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Pebax® MV 2080 | Arkema | PEBA-Ether | Pebax® |